Computational Nanotechnology by Freitas confirms that nanoparts from 1-2 nm nanodiamond components will be structurally stable

The use of precisely applied mechanical forces to induce site-specific chemical transformations is called positional mechanosynthesis, and diamond is an important early target for achieving mechanosynthesis experimentally. The next major experimental milestone may be the mechanosynthetic fabrication of atomically precise 3D structures, creating readily accessible diamond-based nanomechanical components engineered to form desired architectures possessing superlative mechanical strength, stiffness, and strength-to-weight ratio. To help motivate this future experimental work, the present paper addresses the basic stability of nanoscale diamond structures with clean or hydrogenated surfaces that possess certain simple features including ledges, steps, and corners. Computational studies using Density Functional Theory (DFT) with the Car-Parrinello Molecular Dynamics (CPMD) code, consuming ∼2,284,108.97 CPU-hours of runtime on the IBM Blue Gene/P supercomputer (23 TFlops), confirm that fully hydrogenated nanodiamonds 1–2 nm in size possessing ledges with various combinations of convex or concave edgelines where any two of the three principal diamond faces meet will maintain stable sp3 hybridization.

Computational studies using Density Functional Theory (DFT) confirm that fully hydrogenated nanodiamonds 1–2 nm in size (∼900–1700 atoms) possessing ledge features with various combinations of convex or concave edgelines joining any two of the three principal diamond faces will maintain stable sp3 hybridization. This result applies to nanodiamonds with concave ledges that have acute, normal, or obtuse angles or that have step walls that are one or more adamantane cages in height. Convex edgelines seem generally stable, as are concave edgelines formed from the intersection of C(110)-C(110), C(110)-C(111) and C(111)-C(111) surfaces.

We conclude that H-passivated diamond nanoparts having certain simple features including ledges, steps, and corners possess at least static structural stability. These results support the viability of proposals to use such nanoparts as components of nanoscale diamondoid nanomachines and nanomachine systems

If you liked this article, please give it a quick review on ycombinator or StumbleUpon. Thanks